Removal of malachite green from water by Firmiana simplex wood fiber

Xiangliang Pan
Xinjiang Institute of Ecology and Geography
Chinese Academy of Sciences
Urumqi 830011, China

Daoyong Zhang*
State Key Laboratory of Environmental Geochemistry
Institute of Geochemistry
Chinese Academy of Sciences
Guiyang, 550002, China
E-mail: zhang-daoyong@163.com

*Corresponding author

Financial support: Knowledge Innovation Program of Chinese Academy of Sciences (KZCX2-YW-335 and KZCX2-YW-135), Program of 100 Distinguished Young Scientists of the Chinese Academy of Sciences , National Natural Science Foundation of China (40673070, 40872169) and 863 program project 2006AA06Z339 from MOST of China.

Keywords: adsorption, kinetics, malachite green, thermodynamics, wood fiber.

Abbreviations:

MG: malachite green

Abstract  

This study shows that wood fiber of Phoenix tree (Firmiana simplex) is an effective adsorbent for malachite green (MG). MG sorption behavior onto the wood adsorbent was investigated in this study. Basic condition was favorable for MG adsorption to the adsorbent. The pseudo second order equation well described MG adsorption onto the wood adsorbent. The Freundlich Isotherm could describe the sorption data. The positive value of ΔH0 showed that adsorption of malachite green onto the wood adsorbent was endothermic. The negative values of ΔG at various temperatures indicate the spontaneous nature of the adsorption process.  

Article

Malachite green (MG), a triphenylmethane dye, is used as an antifungal, anti-bacterial, and anti-parasitical therapeutic agent in aquacultures and animal husbandry. It is also widely used as a direct dye for silk, wool, jute and leather. Malachite green has detrimental effects on liver, gill, kidney, intestine and gonads of aquatic organisms (Srivastava et al. 2004). When it was inhaled or ingested by human, it may cause irritation to the gastrointestinal tract and even cancer (Garg et al. 2004). Contact of malachite green with skin causes irritation with redness and pain. Intermediate products after degradation of MG are also reported to be carcinogenic (Srivastava et al. 2004). Therefore, the use of malachite green in aquaculture was banned in many countries. However, MG in fishes, animal milk and other foodstuff is still detected due to illegal use of MG (Srivastava et al. 1995), which alarm the health hazards against human being.

Adsorption is the most commonly used method for color removal. Adsorption onto activated carbon is widely practiced for removal of dissolved dyes from wastewater. However, adsorbent-grade activated carbon is cost-prohibitive. So it is necessary to seek some alternative low-cost adsorbents that do not need pretreatment to replace activated carbon (Popuri et al. 2007; Vieira et al. 2007). Recently, a number of low-cost adsorbents for dye removal from mineral wastes (Yener et al. 2006), agricultural wastes, microbial biomass (Aksu, 2005) and higher plant biomass (Ho et al. 2005) were reported in the literature. Among them, biomaterials from higher plants seem to be one type of popular low-cost adsorbents because they usually have higher biomass compared with microbes and are easily available. For example, tree fern (Ho et al. 2005), orange peel (Arami et al. 2005), date pits (Banat et al. 2003), palm kernel fiber, sawdust (Garg et al. 2004), peanut hull (Gong et al. 2005), neem leaf (Bhattacharyy et al. 2003) and de-oiled soya (Mittal et al. 2005) were tested for treatment of dye-bearing wastewaters with different success.

Phoenix tree (Firmiana simplex) is a species of deciduous tree, which grows very fast and is widely spread in China. Its wood had no economic value. The aim of this study was to clarify adsorption behavior of phoenix tree wood fiber for removal of MG from water. The equilibrium, kinetics and thermodynamics of adsorption of MG from water to wood fiber were investigated.

Materials and Methods

Preparation of adsorbent and dye solution

Wood fiber of phoenix tree (Firmiana simplex) was powdered and sieved through a 100-mesh sieve. The powder was soaked in distilled water overnight and rinsed with several times till the wash water contains no color, monitored by a UV-vis spectrometer. The woody powder was air dried and stored in a desiccator for use. pH of the adsorbent was determined by Gindl and Tschegg’s method (2002). Other physicochemical properties were characterized by adopting the standard procedures.

Analytical reagent MG, CI=42000, chemical formula= C50H52N4O8, λmax = 617 nm, purity over 99% was obtained from Shanghai Chemicals Co., China. Since the dye has high purity, we did not take the effect of impurity into account in our study. 1 g L-1 stock solution was prepared with deionized water. All working solutions used in tests were prepared by appropriately diluting the stock solution to a pre-determined concentration. All other chemicals used in this study were analytical reagent.

Sorption studies

The adsorption of malachite green onto the adsorbent was investigated in batch experiments.

Effect of initial solution pH

The effect of pH on dye malachite green sorption was evaluated by adding 0.25 g of adsorbent into flasks containing 100 ml of 100 mg L-1 malachite green solutions at different initial pH (3-11). pH of the solutions was adjusted using 0.1M HCl/NaOH. The adsorbent was added after MG solution pH was fixed. Flasks containing the adsorbent and MG solution were shaken at 300 rpm and 25°C for 180 min. Initial and equilibrium pH of solutions and residual malachite green concentrations were measured.

Effect of adsorbent dosage

Effect of adsorbent dosage was studied by adding different adsorbent doses (0.05-0.25 g) into flasks containing 100 ml of 100 mg L-1 malachite green solutions. The pH of the solutions was preadjusted to 7 according to the result of the study on effect of pH. Flasks were shaken at 300 rpm and 25°C for 180 min. Initial and equilibrium pH of solutions and residual malachite green concentrations in solutions were measured.

Kinetic study

For kinetic sorption experiment, 1.25 g of dry adsorbents were added to flasks containing 500 ml of 100 mg L-1 malachite green-bearing solution with pH adjusted to 7. Flasks were shaken at 300 rpm at predetermined temperature. Aliquot amounts of solution were taken, periodically. Residual malachite green concentrations in solutions were measured.

Isothermal and thermodynamic study

For isotherm analysis, adsorption experiments were conducted by varying the initial malachite green concentration from 10 mg/l to 500 mg L-1. 0.25 g of dry adsorbent were added to flasks containing 100 ml of malachite green-bearing solution with pH preadjusted to 7. Flasks were shaken at 300 rpm and predetermined temperature for 180 min. Residual malachite green concentrations in solutions were measured.

Analytical methods

The samples were centrifuged and malachite green concentrations in supernatant were determined by measuring the absorbance using a spectrophotmeter (UV-2000, Unico, Shanghai, China). pH was measured using a pH meter.

Results and Discussion

Physicochemical properties of the adsorbent

The physico-chemical characteristics of the adsorbent were: apparent density 1.36 g/ml; surface area 226.5 m2/g; Cation exchange capacity (CEC) 0.87 meq/g dry matter; pH 5.1; and EC 0.11 mS/cm.

Effect of initial pH

Figure 1 shows that adsorption percentage of MG increased with increasing pH. The maximum of adsorption percentage of malachite green was observed at pH 11. At lower pH, the number of positively charged adsorbent surface sites increased at the expense of the number of negatively charged surface sites. The carboxylic groups of MG (pKa = 10.3) were protonated and had high positive charge density at a lower pH (Garg et al. 2003; Crini et al. 2007). Consequently, electrostatic repulsion between the positively charged surface and the positively charged dye molecule increased with increasing solution pH and resulted in the decreasing of adsorption capacity of MG to the adsorbent with increasing of pH. In addition, the competition of H+ with the cationic dye molecules due to the presence of excess H+ also decreased the adsorption (Porkodi and Kumar, 2007). On the contrary, the surface of the adsorbent was negatively charged at higher pH, which favored for adsorption of the positively charged dye cations through electrostatic force of attraction. The adsorption of MG to wood fiber consequently increased with increasing of pH values.

A similar trend was observed for the adsorption of MG to cyclodextrin-based adsorbent (Crini et al. 2007), anaerobic granular sludge (Cheng et al. 2008), de-oiled soya (Mittal et al. 2005), hen feathers (Mittal, 2006), rattan sawdust (Hameed and El-Khaiary, 2008a; Hameed and El-Khaiary, 2008b) and rice straw. 

Effect of adsorbent dosage. It is evident from Figure 2 that the removal percentage of malachite green increased on the increasing of the adsorbent dosage. This can be attributed to the increase in surface area with a high dosage of the adsorbent. On the contrary, the sorption capacity decreased from 142.4 mg/g-1 to 35.6 mg/g-1 as adsorbent dosage increased from 0.05 g to 0.25 g. The decrease in sorption capacity may be attributed to the splitting effect of flux (concentration gradient) between sorbate and adsorbent, with increasing adsorbent concentration causing a decrease in amount of malachite green adsorbed onto unit weight of adsorbent. 

Sorption kinetics

Study of sorption kinetics can provide important information on sorption rate and the factors affecting the sorption rate, which is extremely important in designing batch sorption systems. Time courses of malachite green adsorption onto woody fiber were given in Figure 3a. In the present study, pseudo-first order and pseudo-second order models were employed to analyze the kinetics of malachite green adsorption onto the adsorbent.

First-order model

The pseudo-first order equation of Lagergren is generally expressed as follows (Ho and McKay, 1999):

dqt/dt = k1(q1-qt)                      (1)

where q1 and qt are the amount of malachite green adsorbed per unit weight of adsorbent at equilibrium and at time t, respectively (mg/g) and k1  the rate constant of pseudo-first order sorption (l/min). given the boundary conditions for t=0, qt=0, the equation(1) can be integrated to give (Ho and McKay, 1999)

log(q1-qt) = logq1- (k1/2.303)t            (2)

If the sorption process can be described by pseudo-first order equation, there should be good linear relationship between log(q1-q) and t.

In the present study, the plot of log(q1-qt) versus time t and the relationship was not linear over the entire time range (Figure 3b), indicating that more than one mechanism involved in adsorption. The q1, cal obtained from first-order equation was much different from the expected values (qexp) (Table 1).

Second-order model

If the rate of sorption is a second order mechanism, the pseudo-second order chemisorption kinetic rate equation is expressed as (Ho and McKay, 1999)

dqt/dt = k2(q2-qt)2                    (3)

Where q2 is the amount of malachite green adsorbed at equilibrium (mg g-1), k2 is pseudo-second order rate constant (g mg-1 min-1), and qt is the amount of malachite green adsorbed per unit weight of adsorbent at time t. After integrating and applying boundary conditions for t=0, qt=0, equation (3) becomes

t/qt =1/(k2q22)+ t/q2                   (4)

The rate constant k2 can be obtained from the intercept of the linearized pseudo-second order rate equation. If the pseudo-second order equation can fit the sorption data, there should be good linearity between t/qt and t. when t→0, the initial sorption rate u can be defined as

u=k2q22                           (5)

Half-adsorption time (t1/2) is the time required for the adsorption to take up half as much malachite green as its equilibrium value. This time is an indicator for the adsorption rate. It was calculated from the following equation:

t1/2= 1/k2q2                          (6)

Figure 3c showed that the pseudo-second order equation was satisfactorily applicable to all the sorption data (r=0.999). The pseudo second-order sorption constants were summarized in Table 1. The q2, cal calculated from second-order equation was close to the expected values.

MG adsorption kinetics to cyclodextrin-based adsorbent (Crini et al. 2007), Pithophora spp. (Kumar et al. 2005) and carbon (Zhang et al. 2008) were also reported to follow the pesudo second-order equation.

Sorption isotherms

The Freundlich isotherm is a nonlinear model and is shown to be consistent with exponential distribution of active centres, characteristic of heterogeneous surfaces. It is usually expressed as follows:

qe=kFCe1/n                           (7)

where qe is the amount of malachite green adsorbed, mg/g-1(dry mass); Ce is the equilibrium malachite green concentration in solution, mg L-1; kF and n are rate constants, being indicative of the extent of adsorption and the degree of nonlinearity between solution and concentration, respectively. A high value of n is indicative of good adsorption over the entire range of concentrations studied, while small n is indicative of good adsorptin at high concentrations but much less at lower concentrations. A higher value of kF indicates a higher capacity for adsorption than a lower value.

The Freundlich equation describing malachite green adsorption by the wood adsorbent was illustrated in Figure 4, and the Freundlich constants calculated from the linear equations were summarized in Table 2. The Freundlich equations could describe the sorption. However, Kumar and Sivanesan (2007) demonstrated that sorption process of malachite onto rubber wood could not well represented by the linear Freundlich equation but could be well described by the nonlinear Freundlich equation.

The values of the exponent 1/n were in the range of 0-1, indicating favorable adsorption at all temperatures tested. The value of KF increased on increasing of temperature, indicating that higher temperature favored malachite green sorption onto the wood adsorbent. The MG sorption capacity to wood fiber increased on increasing of the temperature. At an initial malachite green concentration of 100 mg/l, the sorption capacity steadily increased from 32.6 mg/g-1 at 278 K to 36.6 mg/g-1 at 308 K, indicating that the process is endothermic in nature and higher temperature was favorable for malachite green adsorption onto adsorbent.

Thermodynamic studies

Analysis of thermodynamics of equilibrium sorption data can give more important information on sorption process. In the present study, thermodynamic parameters were calculated by using the equation (8)

lnKd= ΔS0/R-ΔH0/RT             (8)  

where Kd is the distribution coefficient (ml/g-1), ΔH0 , ΔS0, and T are the enthalpy, entropy, and temperature in kelvin, respectively, and R is the gas constant. ΔH0 and ΔS0 were obtained from the slope and intercept of the plot of lnKd against 1/T (Figure 5). Gibbs free energy ΔG was calculated using the equation (9)

ΔG= ΔH0-TΔS0                 (9)

The values of the thermodynamic parameters for the sorption of malachite green onto adsorbent are given in Table 3. The positive value of ΔH0 showed that adsorption of malachite green onto the wood adsorbent was endothermic. The negative values of ΔG at various temperatures indicate the spontaneous nature of the adsorption process. ΔG decreases with increased temperature indicated that the adsorption was more favorable at higher temperature. The positive value of ΔS0 indicated that the adsorption process was irreversible and random at the solid/liquid interface during the sorption of malachite green onto the wood adsorbent. In addition, the positive value of ΔS0 suggested some structural change of malachite green and the wood adsorbent (Gupta, 1998) and favored complexion and sorption stability (Donat et al. 2005). Similar results were also observed on carbon prepared from Arundo donax root (Zhang et al. 2008) and de-oiled soya (Mittal et al. 2005), bentonite (Bulut et al. 2008) and hen feathers (Mittal, 2006).

Comparison with other adsorbents for MG

Many adsorbents for MG removal, including activated carbon, various biosorbents, minerals, were reported in the literature (e.g., Mall et al. 2005; Kumar, 2006; Malik et al. 2007; Bulut et al. 2008; Zhang et al. 2008). Part of the data of MG sorption capacity (values of qm derived from the Langmuir equation) of various adsorbents, especially the low-cost adsorbents, was summarized in Table 4. In the present study, the experimental value was used due to failure of the Langmuir equation to describe the isothermal sorption data. It was found that Firmiana Simplex wood fiber is an excellent adsorbent for MG. Activated carbon, sometimes, was more effective in sorption of MG than this woody adsorbent. However, activated carbon is cost-prohibitive since a great deal of energy would be consumed during production of activated carbon. On the contrary, Firmiana simplex wood almost costs nothing since it has little economic value and can be directly used as adsorbent without further procedures. In this sense, Firmiana simplex wood fiber is an excellent adsorbent for MG.

Concluding Remarks

The wood adsorbent was an excellent adsorbent for malachite green. The sorption kinetics followed the pseudo second order equation, indicating that several processes were involved in malachite green sorption onto the wood adsorbent. Basic condition was favorable for MG adsorption to the adsorbent. The Freundlich Isotherm satisfactorily described the sorption data. The MG adsorption was a spontaneous endothermic process.

Since Firmiana simplex grows widely in the world and rapidly with great biomass, has little economic values, and has excellent adsorption capacity for MG, Firmiana simplex wood fiber should be a promising and cost-effective adsorbent for MG removal in industry. Further studies on quantitative characterization of this adsorbent and involved mechanisms, and feasibility of using this adsorbent for other triphenylmethane dyes and for its possible industrial application are needed.

Acknowledgements

We would like to express our gratitude to the three anonymous reviewers for their valuable comments that improved the quality of this manuscript.

References

AKSU, Zümriye. Application of biosorption for the removal of organic pollutants: a review. Process Biochemistry, March 2005, vol. 40, no. 3-4, p. 997-1026. [CrossRef]

ARAMI, Mokhtar; YOUSEFI, Limaee Nargess; MAHMOODI, Niyaz Mohammad and TABRIZI, Nooshin Salman. Removal of dyes from colored textile wastewater by orange peel adsorbent: equilibrium and kinetic studies. Journal of Colloid and Interface Science, August 2005, vol. 288, no. 2, p. 371-376. [CrossRef]

BANAT, Fawzi; AL-ASHEH, Sameer and AL-MAKHADMEH, Leema. Evaluation of the use of raw and activated date pits as potential adsorbents for dye containing waters. Process Biochemistry, October 2003, vol. 39, no. 2, p. 193-202. [CrossRef]

BHATTACHARYYA, Krishna G. and SARMA, Arunima. Adsorption characteristics of the dye, Brilliant green, on Neem leaf powder. Dyes and Pigments, June 2003, vol. 57, no. 3, p. 211-222. [CrossRef]

BULUT, Emrah; OZACAR, Mahmut and SENGIL, I. Ayhan. Adsorption of malachite green onto bentonite: equilibrium and kinetic studies and process design. Microporous and Mesoporous Materials, November 2008, vol. 115, no. 3, p. 234-246. [CrossRef]

CHENG, Wen; WANG, Shu-Guang; LU, Lei; GONG, Wenxin; LIU, Xianwei; GAO, Baoyu and ZHANG, Huayong. Removal of malachite green (MG) from aqueous solutions by native and heat-treated anaerobic granular sludge. Biochemical Engineering Journal, May 2008, vol. 39, no.1, p. 538-546. [CrossRef]

CRINI, Gregorio; PEINDY, Harmel Ndongo; GIMBERT, Frédéric and ROBERT, Frederic. Removal of C.I. Basic Green 4 (Malachite Green) from aqueous solutions by adsorption using cyclodextrin-based adsorbent: kinetic and equilibrium studies. Separation and Purification Technology, February 2007, vol. 53, no.1, p. 97-110. [CrossRef]

DONAT, R.; AKDOGAN, A.; ERDEM, E. and CETISLI, H. Thermodynamics of Pb2+ and Ni2+ adsorption onto natural bentonite from aqueous solutions. Journal of Colloid and Interface Science, June 2005, vol. 286, no. 1, p. 43-52. [CrossRef]

GARG, V.K.; KUMAR, R. and GUPTA, R. Removal of malachite green dye from aqueous solution by adsorption using agro-industry waste: a case study of Prosopis cineraria. Dyes and Pigments, July 2004, vol. 62, no. 1, p. 1-10. [CrossRef]

GARG, V.K.; GUPTA, R.; YADAV, A.B. and KUMAR, R. Dye removal from aqueous solution by adsorption on treated sawdust. Bioresource Technologies, September 2003, vol. 89, no. 2, p. 121-124. [CrossRef]

GINDL, Milojka and TSCHEGG, Stefanie. Significance of the acidity of wood to the surface free energy components of different wood species. Langmuir, March 2002, vol. 18, no. 8, p. 3209-3212. [CrossRef]

GONG, Renmin; SUN, Yingzhi; CHEN, Jian; LIU, Huijun and YANG, Chao. Effect of chemical modification on dye adsorption capacity of peanut hull. Dyes and Pigments, December 2005, vol. 67, no. 3, p. 175-181. [CrossRef]

GONG, Renmin; FENG, Min; ZHAO, Jiajing; CAI, Wenkai and LIU, Lingling. Functionalization of sawdust with monosodium glutamate for enhancing its malachite green removal capacity. Bioresource Technology, January 2009, vol. 100, no. 2, p. 975-978. [CrossRef]

GUPTA, Vinod K. Equilibrium uptake, sorption dynamics, process development, and column operations for the removal of copper and nickel from aqueous solution and wastewater using activated slag, a low-cost adsorbent. Industrial and Engineering Chemical Research,January 1998, vol. 37, no. 1, p. 192-202. [CrossRef]

HAMEED, B.H. and EL-KHAIARY, M.I. Equilibrium, kinetics and mechanism of malachite green adsorption on activated carbon prepared from bamboo by K2CO3 activation and subsequent gasification with CO2. Journal of Hazardous Materials, September 2008a, vol. 157, no. 2-3, p. 344-351. [CrossRef]

HAMEED, B.H. and EL-KHAIARY, M.I. Malachite green adsorption by rattan sawdust: Isotherm, kinetic and mechanism modeling. Journal of Hazardous Materials, November 2008b, vol. 159, no. 2-3, p. 574-579. [CrossRef]

HAMDAOUIA,Oualid; SAOUDI, Fethi; CHIHA, Mahdi and NAFFRECHOUX, Emmanuel. Sorption of malachite green by a novel sorbent, dead leaves of plane tree: equilibrium and kinetic modeling. Chemical Engineering Journal, September 2008, vol. 143, no. 1-3, p. 73-84. [CrossRef]

HO, Y.S. and MCKAY, G.A kinetic study of dye sorption by biosorbent waste product pith. Resources, Conservation and Recycling, March 1999, vol. 25, no. 3, p. 171-193 [CrossRef]

HO, Yuh-Shan; CHIANG, Tzu-Hsuan and HSUEH, Yu-Mei. Removal of basic dye from aqueous solution using tree fern as a bioadsorbent. Process Biochemistry, January 2005, vol. 40, no. 1, p. 119-124. [CrossRef]

KUMAR, K. Vasanth. Optimum sorption isotherm by linear and non-linear methods for malachite green onto lemon peel. Dyes and Pigments, 2007, vol. 74, no. 3, p.595-597. [CrossRef]

KUMAR, K.V. and SIVANESAN, S. Isotherms for Malachite Green onto rubber wood (Hevea brasiliensis) sawdust: comparison of linear and non-linear methods. Dyes and Pigments, 2007, vol. 72, no. 1, p. 124-129. [Cross Ref]

KUMAR, K. Vasanth. Comparative analysis of linear and non-linear method of estimating the sorption isotherm parameters for malachite green onto activated carbon. Journal of Hazardous Materials, August 2006, vol. 136, no. 2, p. 197-20. [CrossRef]

KUMAR, K.V.; SIVANESAN, S. and RAMAMURTHY, V. Adsorption of malachite green onto Pithophora sp., a fresh water algae: equilibrium and kinetic modeling. Process Biochemistry, July 2005, vol. 40, no. 8, p. 2865-2872. [CrossRef]

MALIK, R.; RAMTEKE, D.S. and WATE, S.R. Adsorption of malachite green on groundnut shell waste based powdered activated carbon. Waste Management, 2007, vol. 27, no. 9, p. 1129-1138. [CrossRef]

MALL, Indra Deo; SRIVASTAVA, Vimal Chandra; AGARWAL, Nitin Kumar and MISHRA, Indra Mani. Adsorptive removal of malachite green dye from aqueous solution by bagasse fly ash and activated carbon-kinetic study and equilibrium isotherm analyses. Colloids and Surfaces A: Physicochemical and Engineering Aspects, August 2005, vol. 264, no. 1-3, p. 17-28. [CrossRef]

MITTAL, A.; KRISHNAN, L. and GUPTA, V.K. Removal and recovery of malachite green from wastewater using an agricultural waste material, de-oiled soya. Separation and Purification Technology, May 2005, vol. 43, no. 2, p. 125-133. [CrossRef]

MITTAL, Alok. Adsorption kinetics of removal of a toxic dye, Malachite Green, from wastewater by using hen feathers. Journal of Hazardous Materials, May 2006, vol. 133, no. 1-3, p.196-202. [CrossRef]

POPURI, Srinivasa Rao; JAMMALA, Ajithapriya; REDDY, Kachireddy Venkata Naga Suresh and ABBURI, Krishnaiah. Biosorption of hexavalent chromium using tamarind (Tamarindus indica) fruit shell-a comparative study. Electronic Journal of Biotechnology, July 2007, vol. 10, no. 3, p. 358-367. [CrossRef]

PORKODI, K. and KUMAR, K.V. Equilibrium, kinetics and mechanism modeling and simulation of basic and acid dyes sorption onto jute fiber carbon: eosin yellow, malachite green and crystal violet single component systems. Journal of Hazardous Materials,May 2007, vol. 143, no. 1-2, p. 311-327. [CrossRef]

SRIVASTAVA, S.J.; SINGH, N.D.; SRIVASTAVA, A.K. and SINHA, R. Acute toxicity of malachite green and its effects on certain blood parameters of a catfish, Heteropneustes fossilis. Aquatic Toxicology, March 1995, vol. 31, no. 3, p. 241-247. [CrossRef]

SRIVASTAVA, S.; SINHA, R. and ROY, D. Toxicological effects of malachite green. Aquatic Toxicology, February 2004, vol. 66, no. 3, p. 319-329 [CrossRef]

VIEIRA, Denise Mesquita; DA COSTA, Antonio Carlos Augusto; HENRIQUES, Cristiane Assumpção; CARDOSO, Vicelma Luiz andDE FRANCA, Francisca Pessôa. Biosorption of lead by the brown seaweed Sargassum filipendula - batch and continuous pilot studies. Electronic Journal of Biotechnology, July 2007, vol. 10, no. 3, p. 368-375. [Cross Ref]

YENER, Julide; KOPAC, Turkan; DOGU, Gulsen and DOGU, Timur. Adsorption of basic Yellow 28 from aqueous solutions with clinoptilolite and amberlite. Journal of Colloid and Interface Science, February 2006, vol. 294, no. 2, p. 255-264. [Cross Ref]

ZHANG, Jian; LI, Yan; ZHANG, Chenglu and JING, Yuming. Adsorption of malachite green from aqueous solution onto carbon prepared from Arundo donax root. Journal of Hazardous Materials, February 2008, vol. 150, no. 3, p. 774-782. [Cross Ref]

Note: Electronic Journal of Biotechnology is not responsible if on-line references cited on manuscripts are not available any more after the date of publication.

Supported by UNESCO / MIRCEN network